Impact of a mixture of nanofiller and intrinsic pigment on tear strength and hardness of two types of maxillofacial silicone elastomers
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
Background

The ideal maxillofacial prosthesis should have fine and thin boundaries that bind with the surrounding facial structures and possess high tear strength. This study aims to determine the best percentages of nanofiller (TiO2) and intrinsic pigment (silicone functional intrinsic) that could be mixed in as additives to improve the tear strength of Cosmesil M511 and VST50F silicone elastomers with the least effect on their hardness.

Materials and Methods

In this in vitro experimental study, a total of 80 samples, 40 for each elastomer, were fabricated. Each elastomer sample was split into two equal groups to test for tear strength and Shore A hardness. Each group consisted of 20 samples, including 10 control samples without additives and 10 experimental samples with additives (mixtures of 0.2 wt% nano‑TiO2 + 0.25 wt% intrinsic pigment and 0.25 wt% nano‑TiO2 +0.25 wt% intrinsic pigment for the Cosmesil M511 and VST50F silicone elastomers, respectively). Two‑way ANOVA and Tukey test were used for comparison; P < 0.05 was considered statistically significant.

Results

Significant differences in tear strength were found among all tested groups (P < 0.05). The tear strength of the experimental subgroups significantly increased compared with the control subgroups (P < 0.05). Significant differences in Shore A hardness were also observed among all tested groups (P < 0.05) except between the experimental subgroups of both materials, where a nonsignificant difference was obtained (P > 0.05).

Conclusion

Incorporation of select percentages of TiO2 nanofiller and intrinsic pigment into Cosmesil M511 and VST50F silicone elastomers yields improvements in tear strength with a slight increase in hardness.

Language:
English
Published:
Dental Research Journal, Volume:17 Issue: 4, Jul-Aug 2020
Pages:
251 to 257
magiran.com/p2169316  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!