Synthesis and characterization of Cobalt Oxide nanoparticles using Momordica charantia and its photocatalytic activity

Article Type:
Research/Original Article (دارای رتبه معتبر)
Synthesizing plant-derived nanoparticles attract attention due to both their broad-spectrum biological applications and sustainable production. This paper describes the production of Cobalt oxide nanoparticles (Co3O4 NPs) using M. charantia leaf extract. The Uv–Vis absorption spectrum of them has peaks at 309 and 595nm. FTIR spectroscopy reveals bands at 580cm-1 and 667cm-1 and confirms the formation of Co3O4. The particle size was determined by XRD to be between 44.68 and 89.20nm. The Field Emission Scanning Electron Microscopy (FESEM) showed that Co3O4 NPs were irregular in shape and between 40 and 90nm in size. Further, the dye degrading capacity of this nanoparticle was ascertained. The dye degrading capacity of Co3O4 NPs exhibited was 81.50% obtained at 90 minutes of light irradiation.
International Journal of Nano Dimension, Volume:13 Issue: 3, Summer 2022
335 to 343  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!