The Effect of Silica Fume on the Physical Properties of Molten Sulfur Dry Concrete

Article Type:
Research/Original Article (بدون رتبه معتبر)

In this study, we investigated the effect of silica fume with ratios of 10, 20, 30, 40, 50, 60% of the total weight of sulfur dry concrete. After melting at 175 ° C, sulfur powder was mixed with preheated microsilica that reached the level of molten sulfur powder and then poured into molds. In this paper, 189 samples in different forms, including a 10 cm cube for compressive strength test, a 5 cm cube for acid resistance, melting and freezing tests, and a 16 x 4 x 16 cm sample for flexural strength have been prepared. The samples were tested 1, 24 and 72 hours after concreting according to the pre-tests. All samples are stored in the laboratory and poured into molds. An oven in the laboratory was used to bring the sulfur powder to the melting point. Sulfuric acid has been used to test its.

Journal of New Approaches in Civil Engineering, Volume:6 Issue: 2, 2022
45 to 57  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!