Microstructural Evolution of Laser-Clad IN625 Powder on Rene80 Superalloy
Message:
Article Type:
Research/Original Article (بدون رتبه معتبر)
Abstract:

Nickel-based superalloys are one of the main components of fixed and moving blades of land and air gas turbines. Susceptibility of substrate and coating during Rene80 superalloy coating with IN625 was investigated by laser cladding method. For this purpose, the substrate was selected under two conditions of casting and solution heat treatment. Microstructural studies showed that the coating, despite maintaining its hardness due to NbC carbide and Ni2(Cr,Mo) phases, did not form cracks and pores. However, in the coating-substrate interface and heat affected zone of the casting sample, cracking occurred due to the high absorption of process stresses by MC carbide (TiC) and γ´ phase as well as partial melting of these two phases. However, in the case of heat treatment, due to the dissolution of these phases and the low hardness of the substrate, the conditions of non-stress absorption and stress release further reduced the sensitivity to cracking.

Language:
English
Published:
Journal of Environmental Friendly Materials, Volume:6 Issue: 2, Summer-Autumn 2022
Pages:
23 to 26
magiran.com/p2512953  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!