Electrochemical deposition of tin doped zinc selenide (SnZnSe) thin film material

Article Type:
Research/Original Article (دارای رتبه معتبر)
In this research study, the growth of SnZnSe thin film materials was carried out using the cationic precursor, which was an aqueous solution of 0.035 mol solution of ZnSO4.7H2O while the anionic precursor was 0.1 mol solution of selenium metal powder was prepared by dissolving with 4 mL of hydrogen chloride (HCl). The XRD of the films deposited on FTO substrates at different dopant concentration 1%, 2%, 3% and 4% showed the reflection peaks at (220), (221), (300), (310), (311), (222) and (320) with the lattice constant of a=7.189 Ǻ.  The SEM results revealed the random distribution of tiny nano-grains on the substrate, the nano-grains were observed to agglomerate due to the presence of large free energy characteristics of small particles. The optical bandgap of the deposited material enhanced from 2.0-2.3 eV as the dopant concentration increased.
Asian Journal of Nanoscience and Materials, Volume:3 Issue: 3, Jul 2020
189 to 202
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!