(Infiltration of Porous Zircon Preforms With Alumina Precursor (THCHNICAL NOTE
Author(s):
Abstract:
A process is described which involves infiltration of aluminum nitrate into partially sintered (porous) zircon bodies. Infiltration kinetics were studied using infiltration curves with two distinct regions. The final infiltrated samples were sintered at 1600 °C for 2 h and yielded specimens containing the tetragonal zirconia.The experimental results show that in spite of the similar porosity of the infiltrated preform and of pure zircon sintered at 1600 °C, the former has a higher flexural strength and fracture toughness due to the incorporation of the ZrO2 particles and the elongated mullite grains resulting from the infiltration and subsequent heating of the preform.
Language:
English
Published:
International Journal of Engineering, Volume:18 Issue: 3, 2005
Pages:
295 - 300
magiran.com/p315172  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.