فهرست مطالب

Iranian Journal of Materials science and Engineering
Volume:18 Issue: 3, Sep 2021

  • تاریخ انتشار: 1400/08/12
  • تعداد عناوین: 12
|
  • Farid Lekmine, Hachemi Ben Temam, Elhachmi Temam* Page 1

    Nickel phosphorus alloy coatings were prepared by electrodeposition route from sulfate electrolyte bath at various current densities. SEM studies reveal spherical grains covered the entire surface with uniform distribution. EDX results showed a linear increase of P content in the developed deposits with current density and therefore, enhancing the grains size and drop of the hardness values. XRD studies reveal monocrystalline orthorhombic alloys at a low amount of phosphorus (10.88 wt. %). Corrosion tests show that 1 A.dm-2 is the best applied current density giving the nobler Ecorr (-171.4 mV) and the lower icorr (4.64 µA/cm2).

    Keywords: Ni–P alloy coatings, Crystal structure, P content, Hardness, Electrochemical properties
  • Usha Vengatakrishnan, Kalyanaraman Subramanian, Vettumperumal Rajapand, Dhineshbabu Nattanmai Raman* Page 2

    Copper oxide (CuO) nanostructure particles were prepared using KOH/NaOH catalyst by low cost precipitation method and characterized by powder X-ray diffraction (PXRD), scanning electron microscope (SEM) and energy dispersive X-ray spectra (EDX) analysis. The photocatalytic dye degradation study of pure CuO nanostructure particles are analysed against two azo dyes (Direct black 38 (Black-E) and Congo red) under ultraviolet (UV) and solar irradiation. The release of major active species (*OH) in the photocatalytic degradation by as prepared CuO nanostructure particles were investigated by photoluminescence (PL) spectra with two different excitation wavelength (325and 355nm). The band gap of CuO nanostructure particles was calculated from diffuse reflectance spectra. The photocatalytic effect of CuO nanostructure particles is confirmed from the UV – Vis and photoluminescence spectra and also, further confirmed from the kinetic studies under UV and solar radiations. The photocatalytic degradation results revealed that 16.35% and 7.5% of black E and Congo red dye was degraded under UV, while it was 47.2% and 17.6% under solar light. The influence of pH on the photodegradation and change in the reaction temperature under solar irradiation were also analysed

    Keywords: copper oxide, photocatalytic activity, azo dyes, dyedegradation, precipitation method
  • Rabah Bobaaya*, Omar Allaoui, Mokhtar Djendel, Samir Benaniba Page 3

    Coatings based on chromium borides and chromium carbides are commonly employed in applications requiring mechanical performance, such as high hardness and low friction coefficient, as well as corrosion resistance. In this work, we made layers of chromium borides and chromium carbides on the surface of low carbon steel through some specific treatments. For chromium borides, the boriding treatment in a solid medium at 900 °C for 4 hours followed by chromium electroplating on the steel surface and finally the application of annealing treatment at temperatures at 950 °C for 1 and 2 hours. For chromium carbides, the cementation in a solid medium followed by electroplating of chromium on the surface and finally the application of annealing treatment at temperatures between 500 and 1100 °C for 1 hour. The obtained results show that, in the first case, boron diffusion and chromium deposition lead to chromium borides on the treated surface. Similarly, for the second case, the cemented layer and the chromium deposited on the surface combine to form chromium carbides on the treated surface after annealing. The characteristics of the chromium borides and chromium carbides obtained are very similar to those of chromium borides and chromium carbides obtained by other processes.

    Keywords: Chromium, deposition, steel, layer, diffusion, cementation, boriding, annealing
  • Saeed G. Shabestari*, Sahar Ashkvary, Farnaz Yavari Page 4

    The influence of melt superheating treatment on the solidification characteristics and microstructure of Al–20%Mg2Si in-situ composite has been investigated. The results revealed that melt superheating temperature has a significant effect on solidification parameters and morphology of primary Mg2Si particles. Solidification parameters acquired using cooling curve thermal analysis method, indicate that both nucleation temperature and nucleation undercooling of primary Mg2Si particles increase by increasing melt superheating temperature, while recalescence undercooling decrease under the same condition. Also, based on the microstructural evaluations, melt superheating treatment can refine primary Mg2Si particles and alter their morphology from dendritic shape to more spherical shape and the eutectic microstructure of a-Al + Mg2Si becomes finer and the distance between eutectic layers becomes smaller.

    Keywords: Al–20%Mg2Si in-situ composite, melt superheating treatment, cooling curve thermal analysis, microstructure, solidification
  • Umarfarooq Maktedar Abdulkhadar, Patil Somalinganagouda Shivakumargouda*, Gonal Basavaraja Veeresh Kumar, Krishnaraja Govinda Kodancha Page 5

    Residual stress measurement is of utmost importance for the safety and reliability of engineering components and has been an active area of scientific research. Relaxation techniques such as hole drilling, slitting and ring core method are widely applied semi destructive techniques for residual stress measurements in polymer composites. This article reviews the recent literature on the measurement of residual stress in polymer composite by employing the above-mentioned relaxation techniques. This article summarizes the categories of residual stresses, causes of formation, techniques of measurements and also briefly outlines the chronological developments of the Hole drilling and slitting method. The article also provides a comparative summary of these relaxation methods.

    Keywords: Residual stresses, Hole Drilling Method, Slitting Method, Ring core Method
  • Mitra Ghannadi, Hediye Hosseini, Bagher Mohammad Sadeghi, Bahman Mirzakhani*, Mohammad Tahaaha Honaramooz Page 6

    The objective of the present paper is to investigate the effects of rapid heating and cryogenic cooling on on the microstructure and tensile properties of Al-Cu-Mg. The specimens were subjected to three heat treatment cycles in which the Infrared heating (IR) were used as the heating medium at the ageing stage, and the liquid nitrogen and water were used as the quenching mediums. The ageing temperature and time were 190⁰C and from 2 hours to 10 hours, respectively.The results indicated that by using IR at the ageing stage, the hardening rate enhanced because the rapid heating via this method leads to faster diffusion of the alloying elements. Moreover, the high density of nano-sized precipitates formed during ageingleads to higher strength and suitable ductility. Cryogenic treatment showed a negligible effect on both microstructure and tensile properties; however, it improved ductility. Overall, the combination of a high heating rate and cryogenic treatment led to the highest mechanical properties. SEM micrograph of the fracture surface of alloy demonstrated that in Cryogenic treatment+Artificial Ageing (CAA) condition, the surface had been fully covered by deep dimples in contrast to the Cryogenic treatment+Infrared Heating (CIR) and Water-Quench+ Infrared Heating (QIR) conditions which their dimples were shallow and also some facets were observed.

    Keywords: Rapid heating, Cryogenic treatment, Precipitation hardening, Al- Cu-Mg, Tensile properties, Fractography
  • MohammedRuhul Amin Bhuiyan, Hayati Mamur* Page 7

    Carbon-based chemical substances persistence can contribute to adverse health impacts on human lives. It is essential to overcome for treatment purposes. The semiconducting metal oxide is Zinc Oxide (ZnO), which has excellent biocompatibility, good chemical stability, selectivity, sensitivity, non-toxicity, and fast electron transfer characteristics. The ZnO nanoparticles are more efficient compared to other metal oxide materials. Thus, the nanoparticles are in the present research situation to receive increasing attention due to their potential performance of the human body to feel comfortable. The nanoparticles become more promising for biomedical applications through the development of anticancer agents to recovery different types of malignant cells in the human body. The ZnO nanoparticles can be the future potential materials for biomedical applications. The purpose of this paper is to review the cost-effective approach to synthesize the ZnO nanoparticles. Moreover, these ideas can develop for synthesized ZnO biomaterial to perform easily up-scaled in biomedical applications.

    Keywords: Zinc oxide (ZnO), Nanoparticles, Biomedical applications, Cost-effective synthesis, Biomaterials
  • Arian Heidar Alaghband, Azam Moosavi*, Saeid Baghshahi, Ali Khorsandzak Page 8

    Porous nanostructured SnO2 with a sheet-like morphology was synthesized through a simple green substrate-free gelatin-assisted calcination process using Tin tetracholoride pentahydrate as the SnO2 precursor and porcine gelatin as the template. Crystalline phase, morphology, microstructure, and optical characteristics of the as-prepared material were also investigated at different calcination temperatures using X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), UV-visible absorption, and Photoluminescence spectroscopy (PL), respectively. XRD patterns of all the samples revealed the presence of a tetragonal crystalline structure with no other crystalline phases. Moreover, the synthesized hierarchical sheets assembled with nanoparticles displayed a large surface area and porous nanostructure. The calculated optical band gap energy varied from 2.62 to 2.87 eV depending on the calcination temperature. Finally, photoluminescence spectra indicated that the nanostructured SnO2 could exhibit an intensive UV-violet luminescence emission at 396 nm, with shoulders at 374, violet emission peaks at 405 and 414 nm, blue-green emission peak at 486 nm, green emission peak at 534 nm and orange emission peak at 628 nm.

    Keywords: SnO2, Porcine gelatin, Sheet-like morphology, Optical properties, Photoluminescence., Gel drying
  • Hilal Acay*, Ayfer Yıldırım, Ayşe Baran Page 9

    Gold nanoparticles (AuNP) were synthesized using edible mushroom Russula delica (RD) in this study. Possibilities to evaluate these synthesized nanoparticles (RD-AuNPs) as bioactive substances were investigated. Characterization of synthesized RD-AuNPswere characterized via UV-vis, XRD, FTIR, EDX. In spherical view, RD-AuNPs with a crystal size of 34.76 nm were synthesized. As a result, fungal systems used for nanomaterial biosynthesis as an effective alternative to chemical synthesis can be used in different biotechnological and medical applications. RD-AuNPs produced by green synthesis can be evaluated in this context.

    Keywords: AuNPs, fungus, SEM, UV-Vis, XRD, Antimicrobial
  • Amirhosein Paryab, Toktam Godary, Sorosh Abdollahi, Mohsen Anousheh, Adrine Malek Khachatourian* Page 10

    Silicon oxycarbide (SiOC) materials derived from silicone attracted great attention for their superior high-temperature behavior. In the present study, Si(Ti)OC and Si(Ti,Al)OC nanocomposites, in which alkoxide precursors were used with the main silicone precursor, have been compared with SiOC material. Although in SiOC, C was bonded with Si in a carbon-rich SiOC phase, X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) showed that TiC was the preferred state for C atoms upon adding Ti into the system. This claim was also substantiated by Raman spectroscopy, where adding Ti into the system lowered the intensity of the D band, indicating the high affinity of C to form crystalline TiC. In the Si(Ti,Al)OC nanocomposites synthesized by adding AlCl3 into the Si(Ti)OC system, mullite nanocrystals formed a superlattice structure with TiC. UV-vis spectra of the nanocomposites showed Si(Ti,Al)OC with mullite-TiC superlattice had a larger bandgap compared with Si(Ti)OC with only TiC nanocrystals.

    Keywords: SiOC nanocomposite, mullite, TiC, polymer-derived ceramics
  • Hamed Tavakoli, MohammadReza Aboutalebi*, Hossein Seyedein, Seyed Nezameddin Ashrafizadeh Page 11

    Solvent extraction of samarium from aqueous solutions by two different types of extractants, namely D2EHPA and PC88A, in kerosene was investigated. Through identification of speciation diagrams, the chemically stable complexes of samarium in different acidic solutions (H2SO4, HCl and HNO3) were first investigated. Regarding the various types of samarium species in sulfate medium in comparison with other acidic environments, H2SO4 and HNO3 media were chosen to examine the extraction behavior of samarium complexes. Thermodynamic parameters of samarium extraction reactions by D2EHPA and PC88A from aqueous solutions of HNO3 and H2SO4 were calculated as ∆G∘ (D2EHPA-HNO3),  , ∆G∘ (D2EHPA-H2SO4) , ∆G∘ (PC88A-HNO3), ∆G∘ (PC88A-H2SO4)  equal to -5.58, 3.40, 6.70 and 14.26, and respective ΔHº values equal to -9.38, -2.75, 4.01 and 16.95 kJ/mol, respectively. According to the results, D2EHPA seemed to be a more efficient extractant than PC88A and nitric aqueous solution was a better media than the sulfuric one. The synergistic effect of binary extractants revealed that synergistic factors were 2.94 and 5.74 in sulfuric and nitric solutions, respectively, for a D2EHPA:PC88A ratio of 2:3. The compositions of extracted complexes by D2EHPA and PC88A in sulfuric and nitric solutions were SmH3A6 and SmH3B6, respectively. Thermodynamic parameters of extraction reactions were calculated to be Ke equal to 9.513, 0.254, 0.067, and 0.003 and ∆S∘ (D2EHPA-HNO3),  , ∆S∘ (D2EHPA-H2SO4) , ∆S∘ (PC88A-HNO3), ∆S∘ (PC88A-H2SO4) equal to -12.75, -20.64, -9.03, and 9.03 (J mol-1), respectively.

    Keywords: Samarium, Speciation diagram, Solvent Extraction, D2EHPA, PC88A
  • Najwa Gouitaa*, Lamcharfi Taj Dine, Abdi Farid, Ahjyaje Fatima Zahra Page 12

    In this study we have synthesis the Zr substituted BaTi0.80Fe0.20O3 ceramics at different content of Zr from x=0.00 to 0.10 by using the solid-state route. The room temperature X-ray diffraction results confirmed the coexistence of the two tetragonal and hexagonal phases for x ≤ 0.050 of Zr content. While above 0.050 the hexagonal phase disappears in benefit of tetragonal phase. The Raman results confirmed the formation of these phases obtained with XRD. The scanning electron micrographs consist of both spherical and straight grain forms for x=0.000 to 0.075, and only spherical grain form for x=0.100 attributed to the tetragonal phase. Also, the grain size increases accompanied with a decrease in density of ceramics with increasing Zr content up to 0.050 then decreases accompanied with an increase in density. Detailed studies of dielectric permittivity measurement have provided a presence of two anomalies Te and TR-O at different temperatures, with a relaxation phenomenon and diffuse behavior which is very important for ceramic at x=0.075 of Zr content. The dielectric permittivity values of the two anomalies of Zr substituted BaTi0.80Fe0.20O3 ceramics increase with increase of Zr content and the dielectric loss is minimal at x=0.100 of Zr content. The conductivity increases with the increasing of Zr substitution from 0.025 to 0.075 levels while for x = 0.100 the dielectric conductivity decreases.  And the Cole-Cole analysis indicates a negative thermal resistivity coefficient (NTCR) behavior of these materials and an ideal Debye-type behavior.

    Keywords: Solid-state, X-ray diffraction, Raman, dielectric permittivity, anomalies, relaxation, diffuse, conductivity, Cole-Cole