Effect of Chlorhexidine on Micro-Shear Bond Strength of Two Adhesive Systems After Aging

Recurrent caries and low bond strength are the main causes of composite restorations failure. This study sought to assess the effect of chlorhexidine (CHX) on micro-shear bond strength (MSBS) to dentin of a fourth generation adhesive system and a universal bonding agent after aging.
This in vitro study used 32 extracted third molars and 3-5mm thick dentin slices were cut out of each tooth. Specimens were randomly divided into 8 groups. After etching, Scotchbond fourth generation bonding agent or Single Bond universal adhesive was applied on dentin surfaces and Z250 composite cylinders were bonded to the surfaces. In groups B, D, F and H, CHX was applied for 1 minute after etching and prior to the application of bonding agent. The MSBS was measured after 24 hours and four months of water storage at 37C using a micro-tensile tester. The collected data were analyzed using three-way ANOVA.
The Scotchbond yielded significantly higher MSBS than the universal adhesive at 24 hours and four months (P The MSBS of Scotchbond fourth generation bonding agent was generally higher than that of Single Bond universal adhesive. The MSBS of both adhesives decreased over time, however, the application of CHX decelerated the deterioration rate.