In this study, the microstructure and mechanical properties of dissimilar resistance spot welding of AISI 430 steel and S500 MC steel were investigated. To carry out this research, Taguchi's L9 array was used to determine the number of samples and determine the range of variables of each sample, and after welding the samples and performing the shear tensile test, the sample with the highest tensile shear strength (13740 N) and the highest amount of fracture energy (102160 Joules), was considered as the best example; Also, the variables of this sample, i.e., welding current of 12 kW, welding time of 12 cycles, and electrode force of 3 kN, had the highest signal-to-noise values, and these values were chosen among the best range of variables among the proposed variables. Then, a microhardness test was performed on the welded sample with the above variables, and microstructural studies were performed by optical microscope and scanning electron microscope. The hardness of the weld zone was observed to be about 400 Vickers, and the microstructure of the weld metal consisted of ferrite, martensite, and Widmannstatten ferrite.

In this study, the effect of welding heat input on microstructure and mechanical properties of dissimilar joints of API-X42 and API-B pipeline steels was investigated. Evaluation of the microstructures showed that increasing the welding heat input decreased acicular ferrite in weld metal microstructure, while amount of Widmanstatten ferrite, polygonal ferrite and grain boundary ferrite increased. Also, results of microhardness test showed that by increasing the heat input, hardness of weld metal and the heat affected zone decreased. Tensile test results showed that as the heat input increased, fracture transferred from base metal of API-B to the heat affected zone. Impact test results also showed that increasing the welding heat input could sharply drop the impact energy of the heat affected zone for both base metals due to extensive grain growth.