  • Z. Yazdani *, M.R. Toroghinejad, H. Edris
    In this paper, bulk sheets of multilayer Al-Ti composites were fabricated by cold roll bonding (CRB) at 50% thickness reduction and annealing in different conditions. The effects of annealing temperature and time on the bonding features of Ti-Al have been evaluated. The microstructural changes were studied by scanning electron microscopy (SEM) and focus ion beam microscope (FIB). A field emission electron microscopy (FEG-SEM) equipped with an electron backscatter diffraction (EBSD) tool was utilized to evaluate microstructural and textural changes. This study revealed that CRB composites of Ti-Al can produce the TiAl3 in relatively short times at annealing temperatures under the Al melting point. The results showed that just the TiAl3 intermetallic layer formed in the Ti/Al interface by 2 h annealing at 590°C. TiAl3 formation mechanism can be stated as following stages, Al phase elimination, Kirkendall voids formation, Ti and TiAl3 phase's volume increasing, micro-crack creation, and finally, easier formation of TiAl3. Mechanical evaluation of Al/TiAl3/Al layered composite showed that low ductility is related to growth and joining of Kirkendall voids around Al/TiAl3 interface that formed after a 2 h annealing at 590°C. Microstructural characterization by EBSD revealed annealing at this condition led to the creation of Al matrix with large grains (about 60 μm) and polycrystalline TiAl3 intermetallic containing small grains (average 5 μm). One of the main outputs from texture analysis is the recrystallization texture components changing after the formation of the TiAl3 intermetallic compound. The presence of large Ti aluminide particles resulted into the creation of a new strong P recrystallization texture component besides R5 and Q.
    Keywords: EBSD, ODF, recrystallization
بدانید!
  • در این صفحه نام مورد نظر در اسامی نویسندگان مقالات جستجو می‌شود. ممکن است نتایج شامل مطالب نویسندگان هم نام و حتی در رشته‌های مختلف باشد.
  • همه مقالات ترجمه فارسی یا انگلیسی ندارند پس ممکن است مقالاتی باشند که نام نویسنده مورد نظر شما به صورت معادل فارسی یا انگلیسی آن درج شده باشد. در صفحه جستجوی پیشرفته می‌توانید همزمان نام فارسی و انگلیسی نویسنده را درج نمایید.
  • در صورتی که می‌خواهید جستجو را با شرایط متفاوت تکرار کنید به صفحه جستجوی پیشرفته مطالب نشریات مراجعه کنید.
درخواست پشتیبانی - گزارش اشکال