    In this study, the Al–TiC nanocomposite was produced by the mechanical milling and sintering process. Also, the optimization of the milling parameters was performed by the Taguchi method. The X-ray diffraction analysis, scanning electron microscopy, and microhardness test were used to analyze the phase characterization, microstructure, and mechanical properties of the Al–4% TiC nanocomposite. At first, the milling speed, milling time, and ball to powder weight ratio were considered as the input data, and the microhardness was considered as the output value of the Minitab software. According to the design of the experiment, 27 experiments must be performed, which were reduced to 9 by the Taguchi method. After the milling, the powders were subjected to the cold pressing and subsequent sintering at 450 °C. The microhardness results showed that the Al–4% TiC nanocomposite was formed with a maximum microhardness of 271 HV. Furthermore, a proper model was proposed and the results indicated that there was a good agreement between the experimental and predicted microhardness.
    Keywords: Al–4%TiC, X-ray diffraction, Milling parameters, Taguchi method
  • J. Arasteh *
    The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructural changes, microhardness, and density of the Zr-10 wt% Cr alloy were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), microhardness measurement, and the Archimedes method. The results showed that the MA increased the solid solubility of the immiscible powders of Cr and Zr; therefore, the Cr atoms were completely dissolved in the Zr lattice after 24 h of the milling time and the nanostructured Zr(Cr) solid solution was obtained with the high microhardness value of about 491 Hv. Also, the results of the density measurement indicated that the resulted density was close to 98% of the theoretical density.
    Keywords: mechanical alloying, microhardness, NanoStructured, Sintering, Solubility
سامانه نویسندگان
  • دکتر جواد آرسته
    دکتر جواد آرسته
    (1399) دکتری مهندسی مواد و متالورژی، دانشگاه شهید باهنر کرمان
اطلاعات نویسنده(گان) توسط ایشان ثبت و تکمیل شده‌است. برای مشاهده مشخصات و فهرست همه مطالب، صفحه رزومه ایشان را ببینید.
بدانید!
  • در این صفحه نام مورد نظر در اسامی نویسندگان مقالات جستجو می‌شود. ممکن است نتایج شامل مطالب نویسندگان هم نام و حتی در رشته‌های مختلف باشد.
  • همه مقالات ترجمه فارسی یا انگلیسی ندارند پس ممکن است مقالاتی باشند که نام نویسنده مورد نظر شما به صورت معادل فارسی یا انگلیسی آن درج شده باشد. در صفحه جستجوی پیشرفته می‌توانید همزمان نام فارسی و انگلیسی نویسنده را درج نمایید.
  • در صورتی که می‌خواهید جستجو را با شرایط متفاوت تکرار کنید به صفحه جستجوی پیشرفته مطالب نشریات مراجعه کنید.
درخواست پشتیبانی - گزارش اشکال