  • P. Kasaeipoor Naeini, M. Delshad Chermahin *, B. Shayegh Boroujeny, T. Ebadzadeh, M. Nilforoushan, M. Abdollahi
    In the present study, a multiferroic (K0.5Na0.5NbO3)-22.5 Vol. % (BaFe12O19) composite was successfully obtained from conventional sintering (abbreviated as CS) method at 1080 °C. To compare the dielectric properties of the samples, lead-free K0.5Na0.5NbO3 (abbreviated as KNN) piezoceramics were prepared using CS method at 1125 °C. The structure and morphology were determined by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM), and the dielectric properties of samples were also investigated. In the X-ray spectra of composite samples, all peaks related to the KNN and BFO phases were observed without any trace of the second phase. In the SEM images of the composite, the distinct cubic morphology of the KNN phase, indicating the formation of the perovskite structure of the compound, and polygonal grains of the BFO phase were observed. The values of relative density, dielectric coefficient, and loss factor of the lead-free KNN ceramic at the sintering temperature of 1125 °C were measured to be 91 %, 390, and 0.02, respectively. These values at the sintering temperature of 1080 °C were about 92 %, 200, and 0.18, respectively. Although the dielectric properties of KNN-BFO composite were lower than those of pure KNN, the presence of magnetic phase could create magnetic properties and, consequently, multiferroicity in the KNN-BFO composite. The dielectric properties also confirmed that this composite can be regarded as a new multiferroic composite.
    Keywords: Ferroelectric KNN, Ferromagnetic BFO, Multiferroic composites, Dielectric properties
  • مسعود علیزاده*، مهسا سلطانی، اصغر کاظم زاده، آیادا فایقی نیا، تورج عباد زاده

    در این پژوهش از پودر اولیه آلومینیوم به عنوان فاز زمینه کامپوزیت همراه با ذرات نیترید سیلیسیوم به میزان 5، 10 و 15 درصد وزنی و نانو لوله کربنی با درصد وزنی ثابت (25/0% وزنی) استفاده شد. پودرهای مورد نظر با درصد وزنی مشخص در دستگاه اسپکس با هم مخلوط شدند. سپس یک سری از نمونه های تهیه شده تا دمای 400 درجه سانتی گراد و مدت زمان نگهداری 5 دقیقه به کمک پلاسمای جرقه یی سینتر شدند، همچنین یک سری دیگر از نمونه ها بعنوان نمونه های استحکام توسط پرس تک محور در فشار 250 مگاپاسکال شکل داده شدند و در دماهای 600، 700و 800 درجه سانتیگراد در کوره مایکروویو به مدت یک دقیقه در بستر گرافیت سینتر شدند. نتایج حاصل از ارزیابی نمونه ها، نشان می دهد افزودن ذرات نیترید سیلسیوم به میزان 15 درصد وزنی بدون و به همراه نانو لوله های کربنی موجب افزایش استحکام خمشی کامپوزیت زمینه آلومینیوم درکوره مایکروویو در دمای 700 درجه سانتیگراد به میزان 179 مگاپاسکال و 212  مگاپاسکال به ترتیب، می شود. همچنین استحکام نمونه های سینتر شده توسط پلاسمای جرقه ای در دمای 400 درجه سانتیگراد با ترکیب 15 درصدوزنی نیترید سیلسیوم بدون نانولوله های کربنی و به همراه نانولوله های کربنی به ترتیب 249 و 285 مگاپاسکال بدست آمد. نمونه های سینتر شده با استفاده از روش پلاسمای جرقه یی شده (sps) به دلیل اعمال فشار و دما به صورت همزمان ، ریزساختار همگن تر و چگالی نسبی بیشتری را نسبت به نمونه های سینتر شده در کوره مایکروویو از خود نشان می دهند؛

    کلید واژگان: کامپوزیت، سیلیکون نایتراید، نانو لوله کربنی، پلاسمای جرقه یی، مایکروویو
    M.Alizadeh*, M.Soltani, A. Kazemzadeh, A. Faeghinia, T. Ebadzadeh

    In this research, we investigated the effect of addition of carbon nanotube (CNT) and sintering processes on mechanical properties of Al- Si3N4 composites. For this purpose difference samples including 5, 10and 15 wt% of Si3N4 with and without 0.25 wt% CNT were fabricated. Samples were sintered via microwave and spark plsma sintering (SPS) methods. Sintering of samples were done at 400°C and 600, 700, 800 °C for spark plasma sinterng process and microwave, respectively. The results showed that the bending strength of samples including 15% Si3N4 with and without CNT that sintered in microwave have maximum value 179 MPa and 212 MPa respectively. Also the bending strength of samples including 15% Si3N4 with and without CNT that sintered in SPS have maximum value 249 MPa and 285 MPa respectively and these samples have higher density than other samples.Also, results showed that the samples that sintered in sps had maximum density and uniformity structure.

    Keywords: Composite, Si3N4, CNT, SPS, Microwave
  • A. Ahmadi, A. A. Youzbashi, A. Nozad, A. Maghsoudipour, T. Ebadzadeh

    Synthesis of YSZ nanopowder by alkoxide sol-gel method, through two different hydrolysis routes, one under careful control by using acetyacetone as ligand, and the other through basic hydrolysis, was investigated. The synthesized powders were characterized by various analytical techniques such as, XRD, STA, PSA, BET, SEM, and TEM. The results showed that, the YSZ powders prepared through the basic hydrolysis route consist of weakly agglomerated nanosized spherical particles; whereas the products obtained through the controlled hydrolysis route, consist of hard irregular shaped agglomerates. Sinterability of these powders was examined at 1480 °C, which showed that the powder synthesized through the basic hydrolysis route attains a density of 94%, against 60% for the other case. It was therefore concluded that, alkoxide sol-gel method through basic hydrolysis route, can be more suitable for the synthesis of YSZ nanopowder and its subsequent sintering.

    Keywords: Yttria, stabilized zirconia, sol gel, alkoxide, hydrolysis, sintering
  • سید احسان غسالی، رحیم یزدانی راد*، کیوان اسدیان، تورج عبادزاده

    در این پژوهش تاثیر افزودنی کاربید تیتانیوم و همچنین پارامترهای سینتر بر ریزساختار و خواص مکانیکی کامپوزیت آلومینیوم- کاربید سیلیسیم مورد مطالعه قرار گرفت. ذرات کاربید تیتانیوم با متوسط اندازه دانه 5 میکرومتر و به میزان 1، 3، 5 و 7 درصد وزنی به کامپوزیت آلومینیوم - 15 درصد وزنی کاربید سیلیسیم اضافه شدند. نمونه های استحکام توسط پرس تک محور در فشار 240 مگاپاسکال پرس و در دماهای 650، 750، 850 و950 درجه سانتیگراد در کوره معمولی به مدت 1 ساعت و کوره مایکروویو به مدت 1 دقیقه در بستر گرافیت سینتر شدند. چگالی نمونه ها به روش ارشمیدس محاسبه و از نمونه ها تست استحکام خمشی گرفته شد و در پایان الگوی پراش پرتو ایکس و مطالعات ریز ساختاری توسط میکروسکوپ الکترونی روبشی مورد بررسی قرار گرفت. نتایج نشان می دهد افزودن ذرات کاربید تیتانیوم به میزان 7 درصد وزنی موجب افزایش استحکام خمشی به روش سینتر معمولی و سینتر مایکروویو به میزان 140 و 215 مگاپاسکال به ترتیب، می شود. نمونه های سینتر شده در کوره مایکروویو با توجه به صرفه جویی در زمان و انرژی، ریزساختار همگن تر و چگالی بیشتر را نشان می دهند؛ همچنین مطالعات ریزساختاری نشان دهنده توزیع مناسب ذرات تقویت کننده در زمینه آلومینیوم است.

    کلید واژگان: کامپوزیت های آلومینیوم - کاربید سیلیسیم، کاربید تیتانیوم، سینتر مایکروویو
    S.E.Ghasali, R.Yazdani-Rad, K.Asadian, T.Ebadzadeh

    Al-SiC-TiC composites have been produced via conventional and microwave sintering. The initial composition as: SiC 15 wt%، TiC 1، 3، 5 and 7 wt% and Al balance، were compacted with uniaxial press at 240 MPa. Green samples were subjected to sintering at 650، 750، 850 and 950°C for 1 h and 1 min in a conventional sintering method and a microwave، respectively. Results indicated that the optimum bending strength corresponded to the sintering at 950°C for samples with 7 wt% and were 140 MPa and 215MPa for conventional and microwave sintered samples، respectively. The microwave sintered specimens showed more uniform distribution of reinforcement particles and higher density than conventional sintered ones concurrent time and energy saving. SEM studies revealed a homogeneous distribution of carbide phases within the Al matrix.

    Keywords: Aluminum, Metal matrix composite, Silicon carbide, Titanium carbide, Microwave sintering
  • A. Abkhezr, M. Atai, A.A. Behnamghader, L. Solhi, T. Ebadzadeh

    The incorporation of boehmite nano-particles and its effects on the mechanicalproperties and bond strength of an experimental dental adhesive were studied.An adhesive solution containing ethanol, Bis-GMA, TMPTMA, HEMA andphoto-initiator system (camphorquinone and DMAEMA) was prepared. Silanizedboehmite nano-particles were incorporated into the adhesive in different concentrationsof 0, 0.2, 0.5, 1, 2, and 5 weight percentages. The suspensions were ultrasonocated tofacilitate the nano-particle dispersion. Degree of conversion of the adhesive under visiblelight irradiation was determined using FT-IR spectroscopy. Depth of cure, diametraltensile strength, flexural strength, and micro-shear bond strength of the adhesives weremeasured. Scanning electron electron microscopy was utilized to observe the fracturesurface topography.

بدانید!
  • در این صفحه نام مورد نظر در اسامی نویسندگان مقالات جستجو می‌شود. ممکن است نتایج شامل مطالب نویسندگان هم نام و حتی در رشته‌های مختلف باشد.
  • همه مقالات ترجمه فارسی یا انگلیسی ندارند پس ممکن است مقالاتی باشند که نام نویسنده مورد نظر شما به صورت معادل فارسی یا انگلیسی آن درج شده باشد. در صفحه جستجوی پیشرفته می‌توانید همزمان نام فارسی و انگلیسی نویسنده را درج نمایید.
  • در صورتی که می‌خواهید جستجو را با شرایط متفاوت تکرار کنید به صفحه جستجوی پیشرفته مطالب نشریات مراجعه کنید.
درخواست پشتیبانی - گزارش اشکال