Synthesys of Cu-Al2O3 Metal Matrix Nano Composite From Cuo and Al Powders by Using High Energy Planetary Fast Milling
Author(s):
Abstract:
Cu-20%Vol Al2O3 matal matrix nano composite powder has been synthesized by using of high energy planetrary fast milling. Due to high exothermic reaction between CuO and Al powders، direct mixing of powders could not be done therefore، to solve this problem، Cu (Al) solid solution powder has been prepared to prevent against explosion in the milling chamber. It has to be mentioned that the mechanical alloying of Cu and Al (14% At.) with atomic ratio of 6:1 for 50 hours، cause to formation of Cu (Al) solid solution powder. After that CuO powder will be added to the powder mixture and milling will be continued to produce relevant composite after 100 hours. During this process، Al will be extracted from the Cu structure and with reaction by oxygen، will produce Alumina. In the other hand، Cu. (Al) solid solution turns back to the pure Cu. Presence of alumina particles (5~30 nm) have been demonstrated by TEM micrographs.
Language:
Persian
Published:
مجله مواد مهندسی, Volume:1 Issue: 4, 2009
Page:
401
magiran.com/p961969
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!