Effect of MgCl2 Addition on the Kinetics of MA Spinel Formation
Author(s):
Abstract:
In this paper, the effect of MgCl2 addition on the kinetics of MA spinel formation was investigated. For this purpose, the stoichiometric mixture of MgCO3 and calcined aluminum was calcined at 1100 °C for 1 hr. Then, the calcined composition was wet-milled and after addition of 6% MgCl2 the compositions were pressed and fired at 1300 and 1500 °C for different times. Spinel phase content was determined using semi-quantitative phase analysis. With regard to Jander's equation, the rate constant was calculated, and the activation energy was obtained from Arrhenius equation. The results showed that the addition of MgCl2 leads to the acceleration of the spinel formation reaction. Besides, 55.71 Kcal/mol as the activation energy was calculated for the composition containing 6 wt.% MgCl2 compared with 93.06 Kcal/mol for the composition without MgCl2.
Keywords:
Language:
Persian
Published:
Journal of Advanced Materials in Engineering, Volume:33 Issue: 1, 2014
Pages:
93 to 103
magiran.com/p1294718
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!