Fabrication and Characterization of Nano-porous beta-Sialon Ceramic Articles Prepared via Gel-casting

Antenna protection against external factors (e. g. wind، rain، and objects colliding) is done by radome. In addition to acceptable mechanical properties، radome should satisfy suitable electrical properties such as dielectric constant and loss tangent to prevent negative effect on antenna performance. In order to build radome to be utilizing at high temperatures (over 1000 °C)، for flying objects with hypersonic speed (5 to 10 Mach)، engineering ceramics are used. Porosity affects the electrical and mechanical properties of articles. It simultaneously reduces the dielectric constant and flexural strength. In this study porous ceramic articles of beta-Sialon were fabricated by ball milling beta-Sialon powder، monomers and water for 10 hours and under 20 MPa uniaxial pressure. Average porosity size of this sample is 200 nm with 30% of its porosities are below 100 nm. Dielectric constant and loss tangent of this sample with 20% porosity in 8-12 GHz is 5. 3 and 0. 04، respectively.
Iranian Journal of Ceramic Science & Engineering, Volume:3 Issue: 3, 2014
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!