Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY- YSZ powders
Author(s):
Abstract:
In this study, the effects of mechanical milling and YSZ reinforcing on oxidation behavior of CoNiCrAlY coatings were investigated. Various amounts of YSZ particles (0%, 5%, 10% and 15 wt.%) were mixed with commercial CoNiCrAlY powder and milled for 24 hrs. Then, the mechanically milled and commercial powders were deposited on Inconel 617 substrate using High Velocity Oxygen-Fuel (HVOF) process. Freestanding bodies of nanostructured and conventional HVOF CoNiCrAlY coatings were oxidized at 1000 °C for different times to form the thermally grown oxide layer. X-ray diffraction analysis, scanning electron microscopy and X-ray mapping were used to analyze the scales formed on the surface of the oxidized samples. The results showed that nanostructured coatings exhibited higher porosity due to undesirable morphology of feedstock powders. This factor accelerated diffusion rate of oxygen into coating body. On the other hand, undesireable oxidation of nanostructured particles during spraying leads to increase in the oxidation rate of coatings.
Keywords:
Language:
English
Published:
Journal of advanced materials and processing, Volume:3 Issue: 1, Winter 2015
Pages:
51 to 58
magiran.com/p1388974
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!