The formation process of nanocrystalline permalloy by electroplating and optimization the surface conditions for alloy coatings
Author(s):
Abstract:
Permalloy (80%wt. Ni, 20%wt Fe) coatings were electroplated in 25°C by applying current density of 100 mA/cm2 in a bath with the pH of 3.8. A mechanical stirrer (160 RPM) was used during 8 hours electroplating. Saccharin was used as a stress reducing agent and a grain refiner to gain nanocrystalline coatings. The pH of plating was controlled by boric acid as a buffer. The SEM images of surface of coatings indicated the different processes of forming the cauliflower structure including nucleation, three dimension growth and integration of crystals. To study the effects of different parameters on the roughness of coatings, various temperatures (25, 45, 75°C), different times (3, 8 hours), different amounts of saccharin in the bath (10, 5, 3, 1g/L) and two different types of agitation (magnetic and mechanic stirrer) were investigated. The results of roughness test showed that decreasing the plating time and the amount of saccharin in the bath decrease the surface roughness. In addition, increasing the temperature and using magnetic stirrer caused a decline in the surface roughness. Increasing the temperature would also change the alloy composition.
Keywords:
Language:
Persian
Published:
New Materials, Volume:6 Issue: 3, 2016
Pages:
89 to 100
magiran.com/p1563351
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!