The Effect of Mechanical Activation on Microstructure of TiB2-TiC- 15wt% Ni Cermet Synthesized by SHS
Author(s):
Abstract:
Self-propagation high-temperature synthesis due to good properties such as low equipment and the economy is a suitable route for the synthesis of engineering materials. In this study effect of activation on SHS synthesis of TiB2-TiC-Ni cermet with 15 wt% Ni content was investigated. Starting materials were activated 3h and under Ar atmosphere. After activation, green powders pressed to cylindrical shape. Synthesis process was done in the tube furnace at the temperature of 1000°C under Ar flow. XRD pattern shows that nanocrystalline TiB2 and TiC were synthesized. The crystallite size of synthesized samples has been calculated by Rietveld method. The average crystallite size of TiB2 and TiC phase in the sample with 15 wt % Nickel was 68 nm and 30 nm, respectively. Also, SEM images show that activated sample have finer and more uniform microstructure.
Keywords:
TiB2 , TiC composite , Ni , nano cermet , mechanical activation , SHS
Language:
Persian
Published:
Iranian Journal of Ceramic Science & Engineering, Volume:5 Issue: 2, 2016
Pages:
15 to 22
magiran.com/p1635185
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!