Fatigue behavior of nano-grained pure copper processed by equal channel angular rolling

Author(s):

Mostafa Ketabchi , Mohammad Eskandarzadeh

Abstract:
The equal channel angular rolling process was successfully performed on commercial pure copper. After 4 passes of this process, grains with a diameter of about 70- 500 nm were formed. The fatigue test results showed that the ultra-fine grained copper represents a longer lifetime under stress-controlled fatigue. To clarify the formation process of surface damage, morphological changes in the fractured surface were monitored by scanning electron microscopy.
Keywords:

nano , grained copper , severe plastic deformation , equal channel angular rolling , fatigue

Language:
English
Published:
Scientia Iranica, Volume:24 Issue: 2, 2017
Page:
656
magiran.com/p1678446  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information