Facile Synthesis and Spectroscopic Studies of SiO2-Core/ZnS-Shell Nanostructure

SiO2/ZnS core/shell nanostructures have been synthesized at room temperature by a simple wet chemical method. The prepared materials are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), infrared spectroscopy (IR), UV–vis spectroscopic and transmission electron microscopy (TEM) studies. X-ray diffraction pattern exhibits peaks correspond to the cubic phase of ZnS. The morphological studies revealed the uniformity in size distribution with core size of 250 nm and shell thickness of 14 nm. From UV–Vis spectra the band gap energies are calculated. The band gap of ZnS has been determined as 3.70 eV directly from the absorption maximum of ZnS, λmax = 335 nm. The band gap of the bulk ZnS is 3.54 eV.
Chemistry of Solid Materials, Volume:2 Issue: 2, Spring 2015
25 to 31
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!