Creation Effect of Composite Coating Containing Titanium Diboride through Flux Cored Arc Welding on the Wear and Hardening Behaviors of Low Carbon Steel

In this research, 3 layer composite weld containing Titanium diboride (TiB2) on low carbon steel (ST37) was carried out through flux cored arc welding via flux cored electrodes containing 100% TiB2 and 50-50 TiB2-Fe. Then, wear and microhardness tests were used for surviving hardness and wear behavior of samples. The obtained results showed that by increasing volume percent of TiB2 in microstructure, the hardness of layers increased. Also, the highest wear resistance belonged to third layer of sample with 50% TiB2 and thereafter, belonged to first layer of sample with 100% TiB2. The scanning electron microscopic investigation of samples wear surfaces indicated that by increasing volume fraction of TiB2 into layers, the depth wear scratches in the third and second layers decreased and segregation of wear debris in these layers increased, compared with first layer. Also, it was found that by increasing the layers, wear mechanism changed from ploughing to cutting.