Effect of heat treatment and addition of 4‑META to silane on microtensile bond strength of IPS e.max CAD ceramic to resin cement
Article Type:
Research/Original Article (دارای رتبه معتبر)

Silane promotes bonding between ceramic and resin cement. Silane function could be improved by heat treatment and adding 4-Methacryloxyethyl trimellitate anhydride (4-META). The aim of this study was to assess the effect of heat treatment and adding 4‑META to silanes on the microtensile bond strength of IPS e.max CAD ceramic and resin cement.

Materials and Methods

In this in vitro study, 32 IPS e.max CAD blocks (6 mm × 6 mm × 4 mm) were randomly divided into 8 groups of 4. The ceramic surfaces were etched by 10% hydrofluoric (HF) for 20 s, and Clearfil Ceramic Primer Plus, Clearfil Porcelain Bond Activator (CPA) +4‑META, CPA + Clearfil SE Bond (CPA + SE), and Bis‑Silane with and without Oven drying at 100°C for 5 min were applied on the ceramic surfaces as silanes, and then, the ceramics were bonded to composite disks by dual‑cured resin cements. Ultimately, a total of 120 sticks ( 1 mm × 1 mm × 8 mm) were subjected to microtensile bond strength test (15 sticks from each group) and the failure types were assessed by stereomicroscope at 40x. Data were analyzed by two‑sided analysis of variance test and Student’s t‑test the P values were considered to be < 0.05.


The Bis Silane group (two bottles) showed maximum bond strength (P = 0.009). Heat treatment significantly reduced the bond strength in Bis Silane (P = 0.0001); but, in other groups, it did not show significant effect on the bond strength. Adding 4‑META to CPA did not significantly affect the microtensile bond strength of IPS e.max CAD ceramic to resin cement, and there was no difference in mode of failure between groups.


The effect of silane type was significant on the microtensile bond strength of the ceramic to resin cement. The effect of 4‑META on the bond strength was not significant. The interaction between silane type and heat treatment on the bond strength of ceramic to resin cement was also significant.

Dental Research Journal, Volume:16 Issue: 5, Sep-Oct 2019
318 to 326
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!