Fabrication and Investigation of Se-Ge Glass-Ceramics in the Presence of Ga and Sn Additives
Article Type:
Research/Original Article (دارای رتبه معتبر)
The Chalcogenide glasses were fabricated by melting and quenching techniques in the Se-Ge system at the presence of 1mol% Ga and 3, 5, and 7mol% Sn. Differential Scanning Calorimetry (DSC) analysis was conducted to extract the heat treatment of the samples. Fourier Transform Infrared (FTIR) spectroscopy analysis was also performed in a range of 2-16µm. The Glass samples were heat-treated at 450°C for 1-10h. The precipitated nanoparticles were observed using a Field Emission Scanning Electron Microscope (FESEM). The crystal size was reported in the range of 100-1000nm. The precipitated phases were identified using X-ray Diffraction (XRD) analysis on Glass-Ceramics powder. The increase in hardness of the Glass-Ceramics was reported in the range of 200-250Kg.mm-2.
Advanced Ceramics Progress, Volume:5 Issue: 4, Autumn 2019
7 to 11
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!