Investigating of High Temperature Oxidation and Thermal Shock Properties of YSZ/Al2O3 Composite Thermal Barrier Coatings with Alumina Made by Solution Precursor Thermal Spray
In this research, a double layer thermal barrier coating was applied and then an alumina diffusion barrier layer was deposited on the YSZ by two solution precersore plasma and solution precersore flame spraying. High temperature oxidation and thermal shock resistance tests were done at 1100˚C. Microstructure of coatings were studied by optical Microscopy and Field Emission Scanning Electron Microscopy. Comparison of the microstructures of coatings showed that applying of Alumina with the solution precursor flame spray process upgrades the thermal properties. High temperature oxidation and thermal shock resistance of YSZ/Al2O3 coatings with Alumina applied by the solution precersoure thermal spray with the same compound were studied. Findings showed that applying alumina with the solution precursor flame spray process leads to increase the amount of the deposited splats and proper contact between them, causes to decrease the diffusion of O2 and as a result TGO thickness decreases and also thermal shock resistance increases.
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.