The effect of sintering pressure on the wear behavior of bronze (85/15) alloys produced using hip method
Article Type:
Research/Original Article (دارای رتبه معتبر)
In this study, a new material was produced using Hot Isostatic Pressing (HIP) method, upon which Co and Ni in different ratios were added into a CuSn-based (85/15) alloy. HIP method has very important advantages in that it allows pressure and temperature to be applied simultaneously during the process. In the study, constant sintering temperature of 800 °C, a constant sintering time of 15 min, and two different sintering pressures of 20 and 30 MPa were used. The sintering process was performed under a vacuum after the initial burning process. The produced samples were subjected to various metallographic processes as well as SEM and EDS analyses. Afterwards, wear test was carried out on the samples. The study investigated the effects of Ni and Co additions and the sintering pressure on the wear behavior. It was found that as the amount of Co and the sintering pressure increased, the wear resistance increased.
2259 to 2266  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!