Synthesis and Characterization Al2O3/Novolac/Fiberglass Nanocomposite: Modification of Thermal Stability and Thermal Insulation Properties
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
Alumina (Al2O3) nanoparticles were used as the additive for modifying a novolac phenolic resin using the solution mixing method. Different weight percentages of nano alumina 3 and 8 w% were loaded into the resin, called 3ARC and 8ARC nanocomposites, respectively. These nanocomposites were investigated by field emission scanning electron microscopy (FE-SEM), X-ray fluorescence spectroscopy (XRF), energy-dispersive X-ray spectroscopy (EDS), and oxyacetylene flame test (OFT). The FE-SEM images exhibited that at low concentrations (3ARC), the nano alumina particles were dispersed uniformly on the surface of novolac resin; however, at high concentrations, the dispersion was repressed by aggregation in the nanocomposites. OFT proved that with increasing alumina content in the nanocomposite, the back temperature of the sample decreases and thus improves the thermal insulation properties.
Keywords:
Language:
English
Published:
Mechanics of Advanced Composite Structures, Volume:10 Issue: 1, Winter-Spring 2023
Pages:
21 to 28
magiran.com/p2527087
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!