INVESTIGATION ON THE POSSIBILITY OF PARTICLEBOARD PRODUCTION FROM HALOXYLON SP. AND WHEAT STRAW

Particleboard industries are a dynamic industry, that has been established and grown rapidly in Iran. Demand for Particleboard has been increased rapidly due to increase population, thus the possibility of utilization residues from other wood using industries or other lignocellulosic raw materials should be investigated. The boards made for this study contained Haloxylon sp. and wheat straw at 0: 100, 75: 25, 50: 50 and 25: 75 ratios as raw material. Samples of all the boards made were tested by the methods described in DIN 68763 standard, to obtain mean values of bending strength, internal bond strength (IB) and thickness swelling. The results of this study showed that there are no significant statistical differences among each combination for MOR and MOE but with increasing the percentage of wheat straw the MOR of boards was found to increase. There were statistical differences among each combination of IB wheat straw had the lowest IB, where as the highest IB were observed on the boards with 100 percent Haloxylon sp. In addition, samples of each type of board were tested for thickness swelling (T.S) after immersion in water for 2 and 24 hours respectively, and the results indicate that there were statistical differences among each combinations and the lowest thickness swelling value was belong to the boards with 100 percent Haloxylon sp. which had the highest IB. It was also observed that the board made of Haloxylon sp. and wheat straw at with 25: 75 ratio had the highest T.S immersion in water after 2 and 24 hours.