Coating of Titania Nanoparticles on Stainless Steel Using an Alkoxide Precursor
Author(s):
Abstract:
niform nanostructure coating of TiO2 was prepared on 316L stainless steel by sol-gel method using Tetra-n-Butyle Titanat (TBT) as alkoxide material. 316L specimens were coated with the mentioned sol by dip coating method. The influences of preparation condition, pH of sol on TiO2 nanostructure coating were investigated. Their structural properties were examined at various calcination temperatures. The effect of drying cycle and solvent bath on crack reduction and the influence of withdrawal speed onthickness of the film was evaluated. Choosing of alcohol as a drying atmosphere could hinder the cracks formation. 400°C was desirable temperature to obtain nanoparticles from anatase phase. At this temperature it was found that TiO2 films exhibited a uniform anatase structure with particle size of about 15 nm. Prog. Color Colorants Coat. 2(2009), Institute for Color Science and Technology.
Keywords:
Anatase , Nanostructure coating , Sol , gel
Language:
English
Published:
Progress in Color, Colorants and Coatings, Volume:2 Issue: 2, Summer 2009
Pages:
71 to 78
magiran.com/p725286
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!