Evaluation of the Compressive and Diametric Tensile Strength of Two Type Nano and Two Type Hybrid Composites

Message:
Abstract:
Introduction
Restorative materials should be able not to strain under pressure during restoration process or mastication, so their mechanical properties are of high importance. The aim of this study was to evaluate the compressive and diametric tensile strength of hybrid and nanofilled composite restorative materials.
Materials and Methods
Two hybrids (Diafil & Spectrum) and two nanofilled composite (nex com & synergy nano) were used in this in vitro experimental study. Samples were placed in a special circular mold and were light cured. After removing, the samples were stored in a light proof container under distilled water for 1 week. The specimens were then submitted to compressive and diametric tensile test, using universal compression machine at a crosshead speed of 1 mm/min. Data were analyzed using ANOVA and Duncan tests at significant level of 0.05.
Results
There was not any significant difference between the values of compressive strengths of the composites (P>0.05). Nex comp showed the least diametric tensile strength (P<0.05), but no significant difference was detected between the other three materials.
Conclusion
Compressive strength of various composites was about the same, but diametric tensile strength of Nexcomp nanofilled composites was lower than other nanofilled or hybrid composites.
Language:
Persian
Published:
Journal of Mashhad Dental School, Volume:34 Issue: 4, 2010
Page:
281
https://www.magiran.com/p806134  
سامانه نویسندگان
  • Davari، Abdolrahim
    Corresponding Author (1)
    Davari, Abdolrahim
    Professor operative&esthetic dentistry, Shahid Sadoughi University Of Medical Sciences, Yazd, Iran
  • Daaneshkazemi، Alireza
    Author (2)
    Daaneshkazemi, Alireza
    Full Professor operative and esthetic dentistry department, Shahid Sadoughi University Of Medical Sciences, Yazd, Iran
اطلاعات نویسنده(گان) توسط ایشان ثبت و تکمیل شده‌است. برای مشاهده مشخصات و فهرست همه مطالب، صفحه رزومه را ببینید.
مقالات دیگری از این نویسنده (گان)