Corrosion behavior of ZrO2-SiO2-Al2O3 refractories in lead silicate glass melts
Author(s):
Abstract:
The chemical corrosion behavior of fusion cast ZAS (ZrO2-Al2O3-SiO2) refractories inside lead silicate glass melt with 68. 5 wt% PbO content was investigated at temperatures of 1200، 1250، 1300 and 1350ºC. Scanning Electron Microscopy (SEM)، Energy Dispersive Spectroscopy (EDS)، Thickness Reduction and Archimedes Principle were used to evaluate morphology/composition/structure of (corroded and un-corroded) refractory probes. The attack of lead silicate glass melt was taken place by inter-diffusion of the more mobile constituents into glassy matrix. chemical reactions produced a low viscosity secondary glass composition and deteriorated the durability.
Language:
Persian
Published:
مجله مواد مهندسی, Volume:2 Issue: 3, 2010
Page:
215
magiran.com/p976535
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!