Comparison of the Bond Strength of Fiber-Reinforced Composite (FRC) Posts to Radicular Dentin Using Different Adhesive Cement: an in-vitro study

Retention of fiber reinforced composite posts depends on the bond strengthbetween post and cement, and cement and root dentin. The aim of this study is to evaluatethe bond strength of one type of fiber post to radicular dentin with different adhesive cements. Crowns of 44 cariesfree, human premolar were removed 2 mm belowthe CEJ and the roots were endodontically treated, then prepared for post cementation. The samples were randomly divided into 4 groups, group 1: Breeze (self-adhesive), group 2: ED Primer II/Panavia F2 (self-etch), group 3:Prime & Bond NT dual-cure /All-Cem (etch & rinse), and group 4: GC Fuji Plus.After post cementation and composite filling of coronal portion(as manufacturers,s instruction)and thermocycling, each specimen was cut into 2 mm thickness from the middle third of theroot and the push-out bond strength test was performed and failure modes were recorded. Data were analyzed employing ANOVA and post hoc tests (P value< 0.05). Group 4 showed significantly the highest bond strength (12.88±3.44 MPa), while group 1 showed significantly lower bond strength than the other groups (5.25±2.98MPa). Also a statistically significant difference was observed between groups 2 and 3 with group 4.(P value<0.021) Retention of fiber post was affected by cement type. The results also indicated that in GC Fuji Plus the chemical interactions be tween the cement and hydroxyapatite may be important for root dentin bonding. Breeze without any pretreatment procedure cannot obtain the acceptable bond strength.