Surface Modification of Polyester by Nano Titanium Dioxide in Alkaline Media and Their Synergism Effect on the Fabric
Message:
Abstract:
The effect of alkaline hydrolysis with sodium hydroxide on nano titanium dioxide (nano TiO2) adsorption was studied on polyester fabric surface as well as the influence of nano TiO2 on the alkaline hydrolysis of polyester. To do this، the polyester fabrics were treated with different concentrations of nano TiO2 and boiling sodium hydroxide solution for 1 h. The results revealed that alkaline hydrolysis reduced the weight of the fabric، which was more prominent in presence of nano TiO2. Field emission scanning electronic microscope and energy dispersive X-ray confirmed the presence of nano TiO2 on the polyester fabric surface. Increasing sodium hydroxide and nanoTiO2 concentrations led to higher loading of nano particles on the polyester fabric surface. Also، the photocatalytic activity of nano TiO2 particles on the polyester fabric was confirmed by the degradation of methylene blue as a model stain under daylight irradiation. The results indicated that increasing sodium hydroxide and nano TiO2 concentrations led to higher photocatalytic activities of the alkali-treated polyester fabrics. Further، the bending rigidity of the treated polyester fabrics decreased while the water absorption of the fabric improved. Unexpectedly، the tensile strength of the nano TiO2 treated polyester fabrics improved even with the action of alkali and surface hydrolysis that usually produce fabric with lower tensile strength. The synergism influence of nano TiO2 particles in alkali hydrolysis of polyester fabric indicated to lower weight fabrics. Overall، this treatment was considered as another useful property such as higher self-cleaning، hydrophilicity and tensile strength.
Language:
Persian
Published:
Iranian Journal of Polymer Science and Technology, Volume:26 Issue: 5, 2014
Pages:
437 - 450
magiran.com/p1219459  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.