The effect of calcium carbonate particles on the wear behavior of nano-composite gear PA6/PP/Nano CaCO3
Abstract:
Nanocomposite gears based on Polyamide 6/Polypropylene (PA6/PP 67/33) blend containing 2.5 to 10 (wt%) of nano-CaCO3 and 5 (wt%) of maleated polypropylene (PP-g-MAH) as compatibilizer were prepared by injection molding. The wear and temperature of gears were characterized against the time by employing a gear testing rig. The ends of gears working lives at which the permanent deformation was happened and, as a consequence, power transmission interrupted, under output torque 14.8 Nm were obtained. The inclusion of nano-CaCO3 led to the 5 °C reduction of gears working temperatures. The maximum life under the torque of 14.8 Nm, was observed in nanocomposite gears containing 2.5 (wt%) of nano-CaCO3 was nearly 2.5 times higher than that of neat PA6 gears. The raise of gears durability by inclusion of CaCO3 nanoparticles was attributed to the improvements of gear teeth flexural and wear resistances.
Language:
Persian
Published:
Pages:
95 - 106
magiran.com/p1573432  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.