Study of Microstructure and Wear Behavior of in-situ Al/Al3Ti Composite Coating on Commercial Pure Al Produced by Aluminum Cored Wires
Abstract:
In this study, GTAW process and cored wires were used to coat Al/Al3Ti wear resistant composite on a commercial pure Al substrate. Wire drawing process was utilized to produce the cored wires from aluminum strips and a mixture of titanium and aluminum powders. The microstructures and the present phases were investigated by metallographic, SEM equipped with EDS and XRD analysis. Moreover, the hardness and wear resistance of the samples were evaluated. A maximum microhardness value of about 300HV was measured which is 13 times higher than the hardness of the substrate material. The results showed that the coating was composed of Al, Ti as well as Al3Ti. The presence of Al3Ti led to increase in the wear resistance of the coating.
Language:
Persian
Published:
Journal of Metallurgical And Materials Engineering, Volume:27 Issue:2, 2016
Pages:
1 - 8
magiran.com/p1577039  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!