Microleakage of two types of low-shrinkage composite resins in class II cavities on primary molars
Message:
Abstract:
Introduction

 In direct aesthetic restoration, microleakage resulting from polymerization shrinkage of resin composites is still challenging. Different strategies such as maximizing the amount of inorganic filler with prepolymerized filler and different silorane matrixes have introduced to overcome this issue. The aim of this experimental study was to compare the microleakage in low-shrinkage methacrylate-based (Clear fil AP-X) and silorane-based (Filtek P90) composite resins in class II cavities on primary molar teeth.

Materials & Methods

 Classic class II slot cavity preparation was done on 60 healthy human primary molars. Specimens were randomly divided into two groups. For restoring the cavity in group I: methacrylate-based composite resin, and in group II: silorane-based micro-hybrid composite resin were used. The samples were thermocycled and soaked in 2% basic fuchsine dye for 24 h. They were longitudinally sectioned and observed at the gingival margins under ×10 magnification. Scores were assigned upon the amount of dye penetration. The Mann-Whitney U-test through SPSS19.0 was used for statistical analysis of data.

Results

 In both groups, the major of samples showed score 0 of dye penetration. The comparison of gingival margin leakage indicated no significant difference between two groups.

Conclusion

 Both restorative materials, irrespective of their type had microleakage. Given the comparable microleakage of silorane-based (Filtek P90) and low-shrinkage methacrylate-based (Clear fil AP-X) composite resins in Class II cavities of primary molars, the clinical efficacy of both materials seems to be similar.

Article Type:
Research/Original Article
Language:
English
Published:
Caspian Journal of Dental Research, Volume:8 Issue: 2, 2019
Pages:
25 - 31
magiran.com/p2047021  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.