Synthesis and characterization of Gd2O2 S: Tb3+ phosphor powder for X-ray imaging detectors
Gadolinium oxysulfide phosphor doped with trivalent terbium have been synthesized using urea homogenous precipitation and followed by sulfurization at 800 °C under argon atmosphere. Structural and morphological of synthesized phosphor powder were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectrometry (FT-IR). Hexagonal structure of Gd2O2S:Tb3+ phosphor was confirmed by XRD. Compositional analysis were carried out by energy dispersive x-ray (EDX) and particle induced x-ray emission (PIXE). Photoluminescence emission spectra was measured by fluorescent spectrometer. A sedimentation technique is used to deposit the phosphor powder directly on the glass substrate using poly vinyl alcohol as a paste. A number of phosphor layers have been synthesized with the layer thickness ranging from 150 to 268 µm. Measurement results of x-ray conversion efficiency for layers were investigated using 300 kVp X-ray tube in which the maximum light output and contrast were observed for layer with a thickness of 193 µm. Oxysulfide phosphor layer was analyzed by ion beam induced luminescence (IBIL). Emitting of green light from phosphor layer confirm its luminescence property.
Article Type:
Research/Original Article
Journal of Nano Structures, Volume:9 Issue:4, 2019
616 - 622  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!