Effect of Curing Time and Percentage of Concrete Additives on Increasing the Compressive Strength and Shear Strength of Silty Sand Soils

The existence of silty sand in the infrastructure under concrete constructions, hydraulic structures, and irrigation systems has always caused challenges. Improving this kind of soil is always a challenging approach to increase compressive strength and shear stress. There is a conception that adding some extra material such as concrete can increase the stability of this soil against contributed forces. The present study investigated the effects of curing time (3, 7, 14, 21, and 28 days) and different percentages of various additives (3%, 5%, and 7%) on the strength of the silty sand soils. A series of laboratory tests were carried out to measure the Uniaxial Compressive Strength (UCS) and California Bearing Ratio (CBR) by evaluating the effect of additives on the strength parameters of silty sand soil. In total, 299 experimental tests have been conducted in the soil mechanics laboratory of SRBIAU. Results indicated that adding additives such as concrete to silty sand soil improved significantly the compressive strength and shear strength. The comparisons among the experimental test illustrate that due to increasing the curing time, the aforementioned parameters were increased significantly; however, Confix and Bentonite aggregates did not have a marginal effect on the compressive strength and shear strength. Also, after the 21st day of the curing time, the rate of increment of the UCS and CBR reached slightly and then attained a constant value. Also, after this duration, the curing time is an independent factor in the variation of the UCS and CBR tests. Furthermore, the addition of 5% Pozzolana cement and 7% Portland cement with 28 days of curing had the highest CBR number and UCS resistance of 176.26 and 17.58 kg/cm2, respectively. Also, the sketch of the different failure patterns was shown during the curing time. Finally, by increasing the curing time, the behavior of specimens from semi-brittle to brittle made them harder.