Structural and Magnetic Characteristics of Fe72-xCoxCr28 (10<X<22) Microcrystalline Alloys Prepared with the Casting Process

Author(s):

Elham Ghasemi , Majid Tavoosi , Ali Ghasemi , Mohammad Loghman Estarki*

Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:

In the present study, the structural and magnetic characteristics of Fe-Co-Cr system, with 28 at. % of Cr content, during casting, solutioning and thermo-magnetic treatment has been investigated. Based on results, the formation of single α-phase solid solution in the Fe72-xCoxCr28 (10<xThe Co content had negligible effects on magnetic characteristics of Fe62Co10Cr28, Fe60Co12Cr28 and Fe58Co14Cr28 alloys. Fe72-xCoxCr28 (10<x with a constant Cr content of about 28 at. %, were outside the miscibility gap in the equilibrium phase diagram, and therefore TMT had no effect on the final magnetic properties.</x</x

Keywords:

Fe-Cr-Co , casting , magnetic properties

Language:
English
Published:
Iranian Journal of Materials science and Engineering, Volume:20 Issue: 2, Jun 2023
Page:
2
magiran.com/p2581809  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information