Evaluation of microleakage in posterior nanocomposite restorations with three types of different liners
Author(s):
Abstract:
Introduction
Microleakage is one of the most important reasons for the failure of composite resin restorations. Use of liners releases the stresses of polymerization shrinkage. The aim of this study was to evaluate microleakage of posterior nanocomposite restorations with three types of liners. Materials And Methods
In this in vitro study forty-eight sound human premolars were randomly assigned to four groups. Classic class II cavities were prepared with gingival margins 1 mm coronal to the CEJ. Cavities were lined in group I with Filtek Z350 flowabl composite resin، in group II with F2 dual-cured composite resin and in group III with Fiji II LC resin-modified glass-ionomer; no liner was placed in cavities in group IV. All the teeth were restored with a posterior nanocomposite (Filtek Z350) to a thickness of 2 mm using horizontal technique except the teeth in group IV in which first a 1-mm layer was placed، followed by a 2-mm second layer; each layer was light-cured for 40 seconds. The teeth were immersed in 2% fuchsin dye، sectioned mesiodistally and observed under a stereomicroscope for dye penetration. Data was analyzed with non-parametric Kruskal-Wallis and Mann-Whitney tests (α=0. 05). Results
Statistically significant differences were observed between the groups (p value = 0. 048). Group I (lined with flowable composite) exhibited maximum leakage; group III (lined with resin-modified glass-ionomer) exhibited the minimum microleakage، which was significantly different only from Group I (p value = 0. 006). Conclusion
The results of this study indicated that none of the liners under study could thoroughly eliminate microleakage of posterior nanocomposites. No differences were observed in microleakage between the groups with liner application.Keywords:
Language:
Persian
Published:
Journal of Isfahan Dental School, Volume:10 Issue: 1, 2014
Pages:
44 to 52
magiran.com/p1244954
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!