Effect of Incorporating Nano-Hydroxyapatite and Nano-Zinc Oxide into Resin Modified Glass Ionomer Cement on Metal Bracket Debonding
Author(s):
Abstract:
Background And Aim
Fluoride releasing adhesives are favorable for bracket bonding since they decrease the risk of demineralization around orthodontic brackets given that they provide acceptably high shear bond strength (SBS). The aim of this study was to evaluate the SBS of resin-modified glass ionomer cements (RMGIC) reinforced by nano-zinc oxide (NZnO) and nano-hydroxyapatite (NHA) particles in comparison with composite resins. Materials And Methods
In this experimental study, 80 extracted human premolars were used. The teeth were randomly divided into 4 groups as follows: Group 1: Transbond XT as the control group, Group 2: RMGIC (Fuji II LC), Group 3: RMGIC with 5% NHA and Group 4: RMGIC with 2% NZnO. After enamel etching, brackets were bonded. The SBS was calculated for each group. The percentage of adhesive remained on the enamel was quantified by calculating the adhesive remnant index (ARI). The data were analyzed using one-way ANOVA and the Kruskal Wallis test. Results
According to the results of ANOVA, there were no significant differences in SBS of groups (P=0.075). The mean SBS in groups 1 to 4 was 15.43 ± 4.61, 14.95 ± 4.34, 17.97 ± 3.65 and 17.08 ± 3.59 MPa, respectively. According to the Kruskal-Wallis test, there were no significant differences in degree of ARI among groups (P=0.413). Conclusion
The SBS was similar among all groups and adding NZnO and NHA particles had no negative effect on SBS of RMGIC. In all groups, less than half the adhesive remained on the enamel after bond failure.Keywords:
Language:
Persian
Published:
Journal of Islamic Dental Association of IRAN, Volume:27 Issue: 1, 2015
Page:
17
magiran.com/p1438406
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!